Rare earth-iron-nitride;;Permanent magnet

作者:杨俊;周寿增;张茂才;马德青;李佛标;王润;
关键词:Rare earth-iron-nitride;;Permanent magnet;;Stability
单位:Department of Materials University of Science and Technology Beijing,Bering 100083,China,Department of Materials,University of Science and Technology Beijing,Bering 100083,China,Department neodymium prices
http://www.999magnet.com/products/142-neodymium-prices of Materials,University of Science and Technology Beijing,Bering 100083,China,Department of Materials,University of Science and Technology Beijing,Bering 100083,China,Department of Materials,University of Science and Technology Beijing,Bering 100083,China,Department of Materials,University of Science and Technology Beijing,Bering 100083,China,
摘要:<正> The effects of the partial substitution of element M(M=Cr,V,Mn,x=0.05;Zr,Ga,x=0.017;Si,x=0.15;Co,x=0.10)for Fe in samarium-iron-nitride Sm_2(Fe_(1-x)M_x)_(17)N_y compounds on their stabilitiesand Curie temperatures have been studied.It is found that Co,Ga can raise the Curie temperature of thecompounds.The initial decomposition temperatures cannot be raised significantly by all the studied elementsexcept Co.The result contradicts the formation enthalpy consideration.The final decomposition tempera-tures can be raised by all of the substitution elements.The effects of atmospheres on their decomposition be-havior were also studied.The results show that oxidation is the major reason for magnetic deterioration ofthe powder heated in air.Compared with nitrogen atmosphere,argon or vacuum helps to delay the decompo-sition of the compounds.